S275N va S460N EN 10025-3 standarti bo'yicha past haroratlarda foydalanish uchun konstruktiv po'latdir, asosiy farq esa mustahkamlikdir: S460N S275N (275 MPa) ga qaraganda yuqori minimal oqish quvvatini (460 MPa) taqdim etadi, bu esa uni og'irroq binolar va ko'priklar va ko'priklar uchun mos qiladi. S275N umumiy tuzilmalar uchun mo'ljallangan, "N" o'rtacha past haroratlarda (taxminan -20 daraja) mustahkamlikni oshirish uchun normalizatsiyani bildiradi.
S275N ning kimyoviy tarkibi
|
Element |
Belgi |
Min (%) |
Maks (%) |
|---|---|---|---|
|
Uglerod |
C |
- |
0.18 |
|
Silikon |
Si |
- |
0.40 |
|
Marganets |
Mn |
0.50 |
1.50 |
|
Fosfor |
P |
- |
0.035 |
|
Oltingugurt |
S |
- |
0.035 |
|
Azot |
N |
- |
0.015 |
|
Niobiy |
Nb |
- |
0.05 |
|
Vanadiy |
V |
- |
0.05 |
|
Titan |
Ti |
- |
0.05 |
|
alyuminiy |
Al |
0.020 |
- |
|
Mis |
Cu |
- |
0.55 |
|
CEV |
- |
- |
0.40 |
S460N ning kimyoviy tarkibi
|
Element |
Choynak tahlili (maksimal %) |
Mahsulot tahlili (maksimal %) |
|---|---|---|
|
Uglerod (C) |
0.20 |
0.23 |
|
Kremniy (Si) |
0.60 |
0.70 |
|
Marganets (Mn) |
1.70 |
1.80 |
|
Fosfor (P) |
0.025 |
0.035 |
|
Oltingugurt (S) |
0.015 |
0.025 |
|
Azot (N) |
0.025 |
0.030 |
|
Alyuminiy (Al) |
0,020 (daq, jami) |
0,020 (daq, jami) |
|
Niobiy (Nb) |
0.05 |
0.06 |
|
Vanadiy (V) |
0.12 |
0.15 |
|
Titan (Ti) |
0.05 |
0.07 |
S275N ning mexanik xususiyatlari
|
Nominal qalinligi (mm) |
Hosildorlik kuchi ReH Min (MPa) |
Kuchlanish kuchi Rm (MPa) |
Cho'zilish A min (%) |
Charpy KV Uzunlamasına min (J) -20 daraja |
Charpy KV Transvers Min (J) -20 daraja |
|---|---|---|---|---|---|
|
16 dan kam yoki teng |
275 |
370–530 |
23 |
47 |
31 |
|
16 < t 40 dan kichik yoki teng |
265 |
370–530 |
23 |
47 |
31 |
|
40 < t 63 dan kichik yoki teng |
255 |
370–530 |
23 |
47 |
31 |
|
63 < t 80 dan kichik yoki teng |
245 |
370–530 |
22 |
47 |
31 |
|
80 < t 100 dan kichik yoki teng |
235 |
370–530 |
22 |
47 |
31 |
|
100 < t 150 dan kichik yoki teng |
225 |
350–510 |
22 |
47 |
31 |
|
150 < t 200 dan kichik yoki teng |
215 |
350–510 |
22 |
47 |
31 |
|
200 < t 250 dan kichik yoki teng |
195 |
350–510 |
22 |
47 |
31 |
S460N ning mexanik xususiyatlari
|
Qalinligi (mm) |
Hosildorlik kuchi (min, MPa) |
Kuchlanish kuchi (MPa) |
Uzayish (min,%) |
Ta'sir energiyasi (min, J @ -20 daraja) |
|---|---|---|---|---|
|
16 dan kam yoki teng |
460 |
540-720 |
17 |
27 |
|
16<> |
460 |
540-720 |
17 |
27 |
|
40<> |
440 |
570-720 |
17 |
27 |
|
63<> |
400 |
570-720 |
17 |
27 |
|
80<> |
380 |
570-720 |
17 |
27 |
|
100<> |
340 |
540-720 |
18 |
27 |
Asosiy farqlar
Quvvat: S275N ning 275 MPa oquvchanligi bilan solishtirganda (16 mm gacha qalinliklar uchun) S460N 460 MPa oqish kuchi bilan sezilarli darajada kuchliroqdir.
Ilovalar: S460N ogʻir texnika, koʻpriklar va arktik dengiz tuzilmalari kabi yuqori quvvat talablari uchun, S275N esa umumiy binolar va quvurlarda qoʻllaniladi.
Samaradorlik: S460N engilroq dizaynlarni yaratishga imkon beruvchi-vaznga nisbatan{2}}yuqori kuch beradi.
O'xshashliklar
Standart: Ikkalasi ham EN 10025-3 standarti bo'yicha normallashtirilgan (N) strukturaviy po'latdir, sovuq sharoitda yaxshi payvandlanishi va mustahkamligi uchun mo'ljallangan.
Mikrotuzilma: Har ikkalasi ham mustahkamlik uchun-parchalangan mikro tuzilishga ega.