ASTM A302 Grades C and D are manganese-molybdenum (Mn-Mo) alloy steels for boilers and pressure vessels, differing mainly in their nickel content and heat treatment requirements, with Grade D typically having higher nickel for improved properties, both offering excellent strength for high-temperature applications, though Grade C (Mn-Mo-Ni) is often specifically alloyed with nickel for better notch toughness. Both grades aim for similar strength levels (tensile 550-690 MPa, yield >345 MPa) lekin aniq kimyoviy tarkibga va qo'llash xususiyatlariga ega, ayniqsa nikel va issiqlik bilan ishlov berish uchun.
ASTM A302 C sinfining kimyoviy tarkibi
ASTMA302 C darajasiKimyoviy tarkibi | |||||||
Baho | Maksimal element (%) | ||||||
C | Si | Mn | P | S | Al | N | |
A302 C darajasi | 0.20-0.25 | 0,13–0,45 | 1.07-1.62 | 0,035 | 0,035 |
|
|
Nb | V | Ti | Cu | Cr | Ni | Mo | |
|
|
|
|
| 0.37-0.73 | 0,41–0,64 | |
ASTM A302 D sinfining kimyoviy tarkibi
ASTMA302 D darajasiKimyoviy tarkibi | |||||||
Baho | Maksimal element (%) | ||||||
C | Si | Mn | P | S | Al | N | |
A302 D darajasi | 0.20-0.25 | 0,13–0,45 | 1.07-1.62 | 0,035 | 0.035 |
|
|
Nb | V | Ti | Cu | Cr | Ni | Mo | |
|
|
|
|
| 0.67-1.03 | 0,41–0,64 | |
ASTM A302 C sinfining mexanik xususiyatlari
Baho |
| ASTM A302 C darajasiMexanik xususiyat | ||
Qalinligi | Yo'l bering | Kuchlanish | Cho'zilish | |
A302 C darajasi | mm | Min Mpa | Mpa | Min % |
6-50 | 345 | 550-690 | 20% | |
50-200 | 345 | 550-690 | 17% | |
ASTM A302 D sinfining mexanik xususiyatlari
Baho |
| ASTM A302 D darajasiMexanik xususiyat | ||
Qalinligi | Yo'l bering | Kuchlanish | Cho'zilish | |
A302 D darajasi | mm | Min Mpa | Mpa | Min % |
6-50 | 345 | 550-690 | 20% | |
50-200 | 345 | 550-690 | 17% | |
Asosiy farqlar va o'xshashliklar
Tarkibi: ikkalasi ham Mn{0}}Mo po'latdir, lekin C darajasi ko'pincha nikelni (Mn-Mo-Ni) o'z ichiga oladi, D darajasiga esa nikel kiradi, odatda mustahkamligi uchun yuqori konsentratsiyaga ega.
Mexanik xususiyatlar: Ular bir-biriga o'xshash kuch diapazonlariga ega, 550-690 MPa valentlik kuchi va 345 MPa atrofida minimal oqish quvvati.
Ilovalar: neft va gaz loyihalarida payvandlangan qozonlar, saqlash tanklari va issiqlik almashinuvchilari kabi muhim ilovalarda qo'llaniladi.
Issiqlik bilan ishlov berish: Qalinligi 50 mm dan ortiq bo'lgan plitalar odatda normalizatsiya qilinishi kerak va PWHT (-payvanddan keyingi issiqlik bilan ishlov berish) yoki HIC (vodorod qo'zg'atuvchi yorilish) sinovlari kabi qo'shimcha muolajalar qo'llanilishi mumkin.
C darajasi (Mn-Mo-Ni)
Qotishma: marganets-molibden-nikel.
Foyda: Nikel qattiqlikni oshiradi va uni talabchan yuqori haroratli- muhitlarga moslashtiradi.
D darajasi (Mn-Mo-Ni)
Qotishma: marganets-molibden-nikel.
Asosiy xususiyat: C darajasiga nisbatan yuqori nikel tarkibini o'z ichiga oladi, bu uning mexanik xususiyatlarini va mustahkamligini yaxshilaydi.