| 17MN4 kimyoviy tarkibi | |||||||
| Baho | Element maksimal (%) | ||||||
| 17mn4 | C | Si | Mn | P | S | Aldamoq | Kri |
| 0.14-0.20 | 0.40 | 0.90-1.40 | 0.035 | 0.030 | 0.02 | 0.25 | |
| Ku | Ni | Mor | Nb | Ti | V | ||
| 0.3 | 0.3 | 0.10 | 0.01 | 0.03 | 0.03 | ||
| Baho | 17mn4 mexanik mulk | |
| Qalinlik | Yo'l bering | |
| 17mn4 | mm | Min MPa |
| 6-16 | 290 | |
| 16-40 | 285 | |
| 40-60 | 280 | |
| 60-100 | 255 | |
| 100-150 | 230 | |
1. Issiqlikni davolash jarayoni nima talab qilinadi?
Javob:
Standart ishlab chiqarish jarayoni:
Normallashtirish (880-950°C) for thickness >30 mm
- plyonkali holat30 mm dan kam yoki unga teng qalinligi uchun
Ixtiyoriy stressni yumshatish yuladi(580-620 daraja)
Termomexanik boshqaruv jarayoni (TMCP)Yaxshilangan xususiyatlar uchun mavjud
2. 17mn4 uchun qaysi payvandlash protseduralari tavsiya etiladi?
Javob:
Kerakli payvandlash amaliyoti:
Qizdirmoq: 100-150°C (for t>25mm)
Sarflangan materiallar: DIN 8556 E 42 4 B 42 yoki unga teng
Issiqlik kiritish: 1.8-3,2 kj / mm
Harorat doirasi: 250 darajadan kam yoki unga teng
Post - Issiqlik bilan isitish (phat): 580-620°C × 1hr/25mm (for t>35mm)
3. 17mn4 odatda belgilangan?
Javob:
Umumiy dasturlar quyidagilardan iborat:
O'rta - bosimli tomirlar(10-40 bar)
Qozon barabanlari va sarlavhalar
Issiqlik almashish chig'anoqlari
Kimyoviy o'simliklardagi uskunalar texnologik uskunalar
Sanoatdan foydalanish uchun idishlar
O'xshash sinflar bilan taqqoslash
| Baho | Standart | Kuch berish kuchi | Asosiy farq |
|---|---|---|---|
| 17mn4 | Din 17155 | 355 MPa dan katta yoki teng | Optimallashtirilgan MN tarkibiga ega nemis standarti |
| P355gh | En 10028-2 | 355 MPa dan katta yoki teng | Evropa ekvivalenti |
| A516 GR.70 | Askm | 260 MPa dan katta yoki unga teng | AQSh standarti, pasayish kuch |
Issiq teglar: plitalar plitasi, etkazib beruvchilar, zavodlar, plitalar, etkazib beruvchilar, zavod bosim o'tkaziladigan tokchalar uchun mN4 did 17155 17 mn4 mn4