A537CL 1+304 L Klad po'latdagi kimyoviy tarkibi va mexanik mulk
|
A537 1-sinfKimyoviy tarkibi |
|||||||||
|
Baho |
Element maksimal (%) |
||||||||
|
C |
Mn |
P |
S |
Si |
Ku |
Ni |
Kri |
Mor |
|
|
A537 1-sinf |
0.24 |
0.92-1.72 |
0.035 |
0.035 |
0.13-0.55 |
0.38 |
0.28 |
0.29 |
0.09 |
|
Baho |
A537 sinf 3 Mexanik mulk |
|||
|
Qalinlik |
Yo'l bering |
Keskin |
Cho'zish |
|
|
A537 1-sinf |
mm |
Min MPa |
Mpa |
Min% |
|
-65 |
380 |
550-690 |
22 |
|
|
65-100 |
345 |
515-655 |
20 |
|
|
100-150 |
275 |
485-620 |
- |
|
| Baho |
C
|
Mn |
P
|
S
|
Si |
Kri |
Ni | Mor | Ni |
Kooper
|
| 304L(S30403) | 0.030 | 2.0 | 0.045 | 0.030 | 0.75 | 17.5-19.5 | 8.0-12.0 | - | 0.10 | - |
| Baho |
Kuch berish kuchi (N / mm2), min |
Keskinlik kuchi (n / mm2), min |
Elgyonin 2 (50mm),%, min |
|
Sovuq egilish | ||||||
|
Ostenit (xrom {- nikel) (xromlar - Manganes - nikgulel) |
|||||||||||
| 304L(S30403) |
|
|
40 |
|
talab qilinmaydi | ||||||
A537CL 1+304 l cload po'lat plitasi
A537CL 1+304 L KLAD po'lat plitalarida ko'priklar qurishda, magistral qurilish va boshqa muhandislik qurilishida qo'llaniladi.
A537CL 1+304 l klangi po'lat plita boshqa ismi
A537CL 1+304 l klangi po'lat plastinka, A537CCL1 po'lat plastinkasi, 304l po'lat plastinka
A537CL 1+304 l klangi po'lat plita boshqa ismi
UT (ultratovik tekshiruv), Ar (faqat issiqlik), n (normallangan), q + t (z35, z35, z35), uchinchi tomon sinovi (SGS testi), qoplangan yoki bo'yash kabi rasm.
A537CL {{4} 1+304 {}} {}} {}} {}} {}} {}} {}}} {}}} lats Llact po'latini 196 darajaga moslashtirish kerak bo'lsa, Kam - Haroratning qattiqligi ko'rsatkichlari yoki alohida qalinlik kombinatsiyasini sozlash, past haroratli tizim integratsiyasida texnik yordam so'rab so'rov yuboring.